MIL-PRF-23269 Capacitors, Fixed, Glass Dielectric, Established Reliability, General Specification ForThis specification covers the general requirements for established reliability, glass dielectric, fixed capacitors. Capacitors covered by this specification have failure rate levels \(FRL\) established in accordance with MIL-STD-690. These FRL are established at a 90 percent confidence level and maintained at a 10 percent producer\'s risk and are based on life tests performed with rated voltage applied at 125 Deg. C. An acceleration factor of 5:1 has been used to relate life test data obtained at 150 percent of rated voltage at 125 Deg. C to rated voltage at 125 Deg. C. A part per million \(ppm\) quality system is used for documenting and reporting the average outgoing quality of capacitors supplied to this specification. Statistical process control \(SPC\) techniques are required in manufacturing process to minimize variation in production of ER capacitors supplied to the requirements of this specification.

Pages 1 - 2 - 3 - 4 - 5 - 6 - 7 - 8 - 9 - 10 - 11 - 12 - 13


. . . . . . . . . . . . . .
MIL-PRF-23269G
3.20 Fungus. The manufacturer shall certify that all external materials are fungus resistant or shall perform the
test specified in 4.7.16. When tested as specified in 4.7.16, there shall be no evidence of fungus growth on the
external surface of the capacitor.
3.21 Resistance to solvents. When capacitors are tested as specified in 4.7.17, there shall be no evidence of
mechanical damage, and the marking shall remain legible.
Insulation resistance:
Shall be not less than the initial requirement.
*
Capacitance:
Shall change not more than 0.5 percent of nominal value or 0.5 pF, whichever is
greater, from the initial value obtained when measured as specified in 4.7.5.
Dissipation factor:
Shall not exceed the initial requirement.
Visual examination:
There shall be no evidence of mechanical damage.
3.22 Resistance to soldering heat. When tested as specified in 4.7.18, capacitors shall meet the following
requirements:
Insulation resistance:
Shall be not less than the initial requirement.
Capacitance:
Shall change not more than 0.5 percent of nominal value or 0.5 pF, whichever is
greater, from the initial value obtained when measured as specified in 4.7.5.
Dissipation factor:
Shall not exceed the initial requirement.
Visual examination:
There shall be no evidence of mechanical damage
3.23 Moisture resistance. When tested as specified in 4.7.19, capacitors shall meet the following requirements:
Visual examination:
No mechanical damage. Marking shall remain legible.
Insulation resistance:
Unless otherwise specified (see 3.1), not less than 10 percent of the initial 25°C
requirement.
Unless otherwise specified (see 3.1), change not to exceed ±10 percent from initial
Capacitance:
measured value.
3.24 Life. When tested as specified in 4.7.20, capacitors shall meet the following requirements, as applicable.
3.24.1 2,000 hour (qualification inspection) (see 4.7.20.1).
Insulation resistance:
Shall be not less than the initial requirement.
*
Capacitance:
Shall change not more than the percent specified (see 3.1) of nominal value or 0.5 pF,
whichever is greater, from the initial value obtained when measured as specified in
Dissipation factor:
Shall not exceed the value specified (see 3.1).
Visual examination:
There shall be no evidence of mechanical damage.
6



For Parts Inquires submit RFQ to Parts Hangar, Inc.
© Copyright 2015 Integrated Publishing, Inc.
A Service Disabled Veteran Owned Small Business

© Copyright 2015 Integrated Publishing, Inc. Site Design & Marketing by Strategico.