MIL-PRF-39006-20 Capacitors, Fixed, Electrolytic \(Nonsolid Electrolyte\), Tantalum, \(Polarized, Sintered Slug\), 85 Deg. C \(Voltage Derated To 125 Deg. C\), Established Reliability, Style Clr17 \(See Notice 1 For Replacement Information\)

Pages 1 - 2 - 3 - 4 - 5 - 6

MIL-PRF-39006/20A

Salt spray (corrosion): Method 101 of MIL-STD-202, condition B (48 hr).

Solderability: Not applicable.

Terminal strength:

Pull: Method 211 of MIL-STD-202, condition A.

Bend (if required): Method 211 of MIL-STD-202, condition B.

Surge voltage: See table I.

Moisture resistance: Method 106 of MIL-STD-202.

DCL: 125 percent (max) of 25�C value of table I.

ĆCap.: Within �8 percent of initial measurement.

DF: 115 percent (max) of initial requirement.

Dielectric withstanding voltage (DWV): Not applicable.

Insulation resistance (IR): Not applicable.

Low temperature (storage): Method 502 of MIL-STD-810.

DCL: See table I.

ĆCap.: Within �5 percent of initial measurement.

DF: See table I.

Stability at low and high temperatures:

Step 1 (+25�C):

DCL: See table I.

Cap.: Within tolerance of table I value.

DF: See table I.

Step 2 (-55�C):

Imp.: See table I.

ĆCap.: Within percent shown in table I of step 1 value.

Step 3 (+25�C):

DCL: See table I.

ĆCap.: Within �5 percent of step 1 value.

DF: See table I.

Step 4 (+85�C):

DCL: See table I.

ĆCap. - +20 percent of step 1 value (max).

DF: See table I.

Step 5 (+125�C):

DCL: See table I.

ĆCap.: +25 percent of step 1 value (max).

DF: See table I.

Step 6 (+25�C):

DCL: See table I.

ĆCap.: Within �5 percent of step 1 value.

DF: See table I.

Reverse voltage: Not applicable.

Life at 85�C: Method 108 of MIL-STD-202.

2,000-hr (qualification):

DCL: See table I.

ĆCap.: Within �20 percent of initial measurement.

DF: See table I.